The Infona portal uses cookies, i.e. strings of text saved by a browser on the user's device. The portal can access those files and use them to remember the user's data, such as their chosen settings (screen view, interface language, etc.), or their login data. By using the Infona portal the user accepts automatic saving and using this information for portal operation purposes. More information on the subject can be found in the Privacy Policy and Terms of Service. By closing this window the user confirms that they have read the information on cookie usage, and they accept the privacy policy and the way cookies are used by the portal. You can change the cookie settings in your browser.
The influence of the cooling rate and the type of under bump metallization (UBM, i.e., Cu and Ni) on the undercooling and solidification behavior of Sn-Ag-Cu (SAC) based solders (i.e., Sn-1.0Ag-0.5Cu, Sn-3.0Ag-0.5Cu and Sn-3.8Ag-0.7Cu) and their joints was characterized. The results show that the cooling rate has little influence on the undercooling of Sn-1.0Ag-0.5Cu and Sn-3.0Ag-0.5Cu solder balls,...
Sn-Bi-Zn lead free solder alloy was directionally solidified upward at a constant temperature gradient (G=3.99 K/mm) with a wide range of growth rates (8.3–478.6 μm/s) and at a constant growth rate (V=8.3 μm/s) with a wide range of temperature gradients (1.78–3.99 K/mm) using a Bridgman type directional solidification furnace. Wavelength-Dispersive X-ray Fluorescence spectrometry and X-ray diffraction...
Effect of solidification cooling rate on Ag3Sn formation and its morphological appearance in Sn-Ag based lead-free solder was investigated. Depends on cooling rate, three types of Ag3Sn compound with different morphologies may form by solidification. They are particle-like, needle-like, and platelike respectively. Small particle-like Ag3Sn in large amount was occurred by rapid cooling, where plate...
This paper deals with presentation of some new aspects of solder ternary alloy 96.5Sn3Ag0.5Cu (wt.%) - SAC305, in order to determine variations in mechanical properties and microstructure caused by treatment in vapour phase soldering (VPS) as well as by accelerated isothermal aging. These specimens have been melted and solidified on HASL (hot air solder levelling) and Ni/Au (ENIG) PCB (printed circuit...
The goal of this research is to evaluate the effects of La addition on the microstructure and microhardness of Sn-Ag based solders. Sn-3.5Ag-xLa ternary alloy solder were prepared by adding 0-1.0 wt% La into a Sn-3.5Ag alloy. Copper substrates were then dipped into these solders and aged at 150degC for up to 625 hours. The microstructure and microhardness of the as solidified solder and the aged solder/copper...