CoxFe3−xO4 (x=0.5–2.5) magnetic nanoparticles were synthesized via redox reaction between cobalt nitrate, iron nitrate and 1-4-butanediol using five Co/Fe molar ratios, followed by calcination at 1000°C. Single phase nanoscaled cobalt ferrite was obtained at x=1.0 and at slight Co excess (x=1.5), while at high Co/Fe molar ratios (x=2.0 and x=2.5) the prevailing phase was CoO accompanied by CoFe2O4 traces. The highest values of coercive field and saturation magnetization were obtained for the sample at x=1.0, while the lowest values were obtained in the sample with the highest Co excess (x=2.5). The results indicated that the used synthesis route was suitable for the synthesis of cobalt ferrite with moderate saturation magnetization and high coercive field values.