Stabilized nano-amorphous calcium phosphate (nACP) was prepared using polyethylene glycol as stabilizer to obtain a nanosized amorphous adsorbent. The produced nACP was evaluated by using XRD, FTIR, SEM and X-ray photoelectron spectroscopy (XPS). The sedimentation test demonstrated that nACP exhibited better stability than crystallized hydroxyapatite. The adsorption efficiency of the nACP material for aqueous humic acid (HA) was evaluated from the point of view of medium pH, adsorption time, temperature, and ionic strength, as well as the presences of metal ions. The results of the study showed very good adsorption performance towards aqueous HA. The Sips modeling results revealed that the stabilized nACP adsorbent had a considerably high adsorption capacity (248.3mg/g) for HA at 298K. The adsorption data fitted well into pseudo-second order and Elovich kinetic models. XPS analyses indicated that HA retention on nACP material might be due to the surface complexation reaction between oxygen-containing group and calcium of HA and nACP, respectively. Moreover, the HA adsorption capacity of nACP could still keep more than 86% after four adsorption-desorption cycles. By taking into account all results it was concluded that the nACP adsorbent leveraged its stability in combination with its high uptake capacity to offer a great promise for HA adsorption from water.