Biaxial cube texturing and surface quality of the metallic substrate are key parameters for high J c coated conductors. Experiments have demonstrated that the sharp cube texture can be developed up to 11 at.% V, 12 at.% Cr and 5 at.% W alloys; the respective cube textured area fractions result to be 96%, 97% and 99%. For all the studied alloys, FWHM values of ω- and φ-scans are in the range of 5-6 o and 6-8 o , respectively. Microstructural analyses reveal smooth surfaces with grooves localized at the grain boundaries of twinned cube textured and misoriented grains.