Purpose
To investigate the influence of reducing material thickness on flexural properties of computer‐aided design and computer‐aided manufacturing (CAD‐CAM) denture base resins.
Materials and methods
Four CAD‐CAM denture base acrylic resin materials were selected; two were made via the subtractive method (AvaDent and IvoCad) and two were made with the additive method (FormLabs and NextDent). One heat‐polymerized denture base material was used as a control. Specimens were fabricated with varying thicknesses (n = 10/group): 3.3 mm, 2.5 mm, 2 mm, or 1.5 mm. Flexural strength was evaluated via a three‐point bending test. One‐ and two‐way ANOVA were used for data analysis along with Tukey's post hoc comparison (α = 0.05).
Results
Reducing the thickness of materials made via the subtractive method did not influence flexural strength up to 2 mm (p > 0.05). However, the difference was significant at a 1.5 mm thickness (p ˂ 0.001). For materials made via the additive method, NextDent specimens had no significant decrease in flexural strength when the thickness was reduced to 2 mm (p = 0.58). FormLabs specimens showed a significant decrease (p ˂ 0.001), although the values of flexural strength were clinically acceptable. During testing, specimens manufactured via the additive method at a 1.5 mm thickness bent without fracturing and were therefore excluded. All materials showed a reduction in elastic modulus as the thickness decreased (p ˂ 0.001).
Conclusion
Heat‐polymerized, AvaDent, and IvoCad materials may be used for denture base fabrication at a minimum thickness of 1.5 mm. FormLabs and NextDent may be fabricated at a 2 mm minimum thickness, with clinically acceptable flexural properties.