Bulk superconducting samples of type GdBa2Cu3−x Ru x O7−δ , Gd-123, with x=0.0–0.3 were prepared by the conventional solid-state reaction technique. X-ray powder diffraction (XRD), scanning electron microscope (SEM), electron dispersive X-ray (EDX) and electrical-resistivity measurements were performed in order to investigate the effect of Ru4+ ions substitution on Gd-123 phase. Enhancement of both phase formation and the superconducting transition temperature T c for GdBa2Cu3−x Ru x O7−δ phase up to x=0.05 was observed from XRD and electrical-resistivity measurement, respectively. This enhancement was confirmed with the calculated relative volume fraction. For x>0.05, suppression of both phase formation and T c was obtained and the superconductivity was completely destroyed around x=0.3. The normal-state electrical resistivity was analyzed by the two- and three-dimensional variable range hopping (2D-VRH and 3D-VRH) and Coulomb gap CG. The results showed that the dominant mechanism was CG for x≤0.075, while was 3D-VRH for x≥0.15.