Ultrafine MgAl2O4 powder has been synthesized by a polymerized complex method. Heating of a precursor solution containing citric acid (CA), ethylene glycol (EG) and Mg and Al salts with a molar ratio of Mg/Al/CA/EG=1/2/8/32 at 180°C produced a transparent polymeric gel, which have been characterized by FT-IR spectroscopy and TG/DTA. The organic fraction was removed by controlled thermal treatments (350–1200°C) whereby the bimetallic oxide was formed. XRD analysis showed the presence of MgAl2O4 at 600°C. TEM observation showed that the spherical nanosized powders with good uniformity was obtained. Furthermore, these powders showed excellent sinterability, relative density up to 99.8% was achieved when sintered at 1550°C for 3 h in air without any sintering additive.