Crofer22 APU specimens were prepared by grinding with grit 120 and 400 SiC grinding papers, and were then thermally cycled. The variation in oxidation behavior with thermal cycling was then investigated. Observation of microstructures, measurement of area-specific resistance (ASR), analysis of the atomic percentages of the elements by EDX, and XRD analysis were performed. XRD patterns showed that the (Cr, Mn)3O4 spinel phase grew on the surface of the Crofer22 APU samples ground using grit 120. For the samples ground with grit 400, ASR increased as the number of thermal cycles (n) increased. Plots of ln (ASR/T) vs. 1/T for the samples ground with grit 400 after n = 4, 20, and 40 exhibited good linearity, and the apparent activation energies were between 73.4 kJ/mole and 82.5 kJ/mole.