Crofer22 APU specimens were prepared by grinding with grit 80 and 120 SiC grinding papers and were thermally cycled. The variation in oxidation behavior with thermal cycling was then investigated. Observation of microstructure, measurement of area specific resistance (ASR), analysis of the atomic percentages of the elements by EDX, and XRD analysis were performed. XRD patterns showed that the (Cr, Mn)3O4 spinel phase grew on the surface of the Crofer22 APU samples ground with grit 120. For the samples ground with grit 80, the ASR increased as the number of thermal cycles increased. Plots of ln (ASR/T) vs. 1/T for the samples ground with grit 80 after n = 4, 20 and 40 exhibited good linearity, and the apparent activation energies were between 63.7 kJ/mole and 76.3 kJ/mole.