Nano transparent conductive oxide (TCO) Ga-doped ZnO (GZO) thin films with thickness from 260 nm to 620 nm were prepared on glass substrates by RF magnetron sputtering from a powder target with 3 at.% Ga2O3. The substrate temperature was kept at 300 °C. The effect of thickness on the structural, electrical, and optical properties of GZO thin films was investigated. It shows that the nano-GZO films are dense and flat, and have polycrystalline structure with preferentially in the (002) orientation. With the increase of thickness, the crystallinity and the grain sizes of the films are improved, meanwhile the carrier concentration increases and the lowest resistivity of 3.685×10−3 Ω cm occurs in the 620 nm thick GZO film. The average optical transmittance of all the films is over 80% in the visible range. Decreasing the thickness, the optical transmission of the films increase, and the absorption edge shifts to shorter wavelength, which means the optical band gap is broadened.