Experiments were conducted to determine the age-hardening characteristics and the mechanical properties of an Al-5.5 pct Mg-2.2 pct Li-0.12 pct Zr alloy processed by equal-channel angular (ECA) pressing to give a very fine grain size of ∼1.2 µm. The results show that peak aging occurs more rapidly when the grain size is very fine, and this effect is interpreted in terms of the higher volume of precipitate-free zones in the fine-grained material. Mechanical testing demonstrates that the ECA-pressed material exhibits high strength and good ductility at room temperature compared to conventional Al alloys containing Li. Elongations of up to ∼550 pct may be achieved at an elevated temperature of 603 K in the ECA-pressed condition, thereby confirming that, in this condition, the alloy may be a suitable candidate material for use in superplastic forming operations.