The diamond-like carbon (DLC) multilayer films have been deposited by plasma CVD deposition onSi wafer substrate. The deposited films have then been post-annealed in vacuum at 250 °C for 2 h. Changes in internal stress, hardness, critical load, friction coefficient and wear have been investigated toassess the influence of annealing on mechanical and tribological properties of DLC multilayer films. At the same time, DLC single layerfilms are also deposited and annealed in the same method for a comparison.The results show that there is 28–33% decrease in internal stress and 10–13% decrease in hardness of theDLC single layer films after the anneal treatment. However, for the DLC multilayer films, there is 41–43% decreasein internal stress and less than 2% decrease in hardness. In addition, the annealed DLC multilayer filmhas the same friction and wear properties as that un-annealed film. This result indicates that the anneal treatment isan effective method for the DLC multilayer films to reduce the internal stress and to increase the critical load.The by-effect of the annealing, decrease of hardness and wear resistance of the multilayer film, can be restrictedby the multilayer structure.