(1 − x)(Bi 0.5 Na 0.5 )TiO 3 /xCoFe 2 O 4 composites with x = 0, 0.1, 0.2, 0.3, 0.4 and 0.5 were synthesized by solid state reaction method. Presence of distinct ferroelectric (Bi 0.5 Na 0.5 )TiO 3 and ferrite CoFe 2 O 4 phases in the prepared composites have been confirmed by the X-ray diffraction analysis and field emission scanning electron micrographs. The variation of dielectric constant with temperature for these prepared composites show an anomaly near antiferroelectric to paraelectric phase transition temperature (∼345 °C) of pure (Bi 0.5 Na 0.5 )TiO 3 ceramics. The dielectric constant of the composites at low frequency range decreases with increase in CoFe 2 O 4 content up to x = 0.3 but increases for x = 0.4 and x = 0.5. The value of remnant magnetization for 10 and 50% CoFe 2 O 4 are 2 and 14 emu g −1 respectively. The maximum value of magnetocapacitance was found to be ∼4.37% for 50% CoFe 2 O 4 content. Increase in CoFe 2 O 4 content in composites shifts the optical band gap of (Bi 0.5 Na 0.5 )TiO 3 towards lower energy side.