Activated carbons were produced from agricultural waste corncob using a variety of different activation strategies and activators. The BET specific surface area and pore volume of the carbons produced by a two-step KOH activation process were 3012m 2 /g and 1.7cm 3 /g, respectively. All carbons prepared showed a microporous character, except for that prepared by a one-step phosphorous acid activation which exhibited hysteresis of a mesoporous carbon. The hydrogen adsorption performance of the different carbons was closely investigated. The microporous carbon with the largest BET specific surface area showed H 2 adsorption capacities up to 2.0wt% at 77K under 1atm pressure and 0.44wt% at 298K at 5MPa. The adsorption isotherm model based on the Langmuir–Freundlich equation together with Soave–Redlich–Kwong equation of state for determination of the gas phase fugacity provided a satisfactory representation of the high pressure hydrogen data. The parameter representing full coverage of the solid surface from the Langmuir–Freundlich equation is 9.73mmol/g or 2wt% at 298K. The carbon with the largest hydrogen uptake capacity still cannot meet the US DOE target for hydrogen storage of 6wt%. The isosteric heat of adsorption of carbon was 7kJ/mol, typical of a physisorption character and in agreement with literature for the hydrogen–carbon interaction.