Amorphous Si–(B–)C–N polymer-derived ceramics (PDCs) with a boron content ranging from 0 to 8.3at.%, were synthesized by thermolysis of boron-modified poly(methylvinylsilazane). Correlation of the boron content and the thermal stability of these materials in the course of annealing were investigated using high temperature thermal gravimetric analysis (HT-TGA). Furthermore, the initial crystallization of the as-thermolyzed amorphous ceramics was studied by X-ray diffraction (XRD) measurements. The increase of boron content promotes the crystallization of SiC, and inhibits the crystallization of Si 3 N 4 . Moreover, the ratio of α-Si 3 N 4 /β-Si 3 N 4 in crystalline ceramic decreases with increasing boron content. Thermodynamic modeling proves the influence of boron content on driving force for crystallization. The available thermodynamic model of amorphous Si–C–N domains, nano-crystalline silicon nitride, and nano-crystalline silicon carbide treated as the separated phases has been used to interpret these results.