Photo- and cathodo-luminescence measurements of a variable-diameter ensemble of GaN nanowires revealed a diameter-dependent, spectral emission distribution between 350 nm and 850 nm. Spectral analysis indicated that wires with a diameter less than 400nm were dominated by a yellow luminescence with a weaker near UV/violet emission also present. Examination of this ensemble showed that there was a general trend in the ratio of near-UV-to-yellow emission intensities with increasing nanowire diameter. Additionally, a broad green emission appears in the nanowires with a diameter above approximately 200nm. A calculation based on the nanoheteroepitaxy model indicates that this diameter represents a transitional thickness where strain is relieved by defect formation mechanisms with a characteristic green emission.