A new method for the fixation of polymethacrylate monoliths within titanium tubing of up to 0.8mm I.D. for use as a chromatographic column under elevated temperatures and pressures is described. The preparation of butyl methacrylate–ethylene dimethacrylate-based monolithic stationary phases with desired porous structures was achieved within titanium tubing with pre-oxidised internal walls. The oxidised titanium surface was subsequently silanised with 3-trimethoxysilylpropyl methacrylate resulting in tight bonding of butyl methacrylate porous monolith to the internal walls, providing stationary phase stability at column temperatures up to 110°C and at operating column pressure drops of >28MPa. The titanium housed monoliths exhibited a uniform and dense porous structure, which provided peak efficiencies of up to 59,000 theoretical plates per meter when evaluated for the separation of small molecules in reversed-phase mode, under optimal conditions (achieved at 15μL/min and temperature of 110°C for naphthalene with a retention factor, k=0.58). The developed column was applied to the reversed-phase isocratic separation of a text mixture of pesticides.