The fabrication of high density (Th, U)O 2 pellets by the sol-gel microsphere pelletization (SGMP) process was studied. To prepare source ThO 2 -UO 3 microspheres, isopropyl alcohol was substituted for the water in gel and thereafter removed by evacuating and subsequently by heating at 200°C in air. After humidifying the microspheres up to the moisture content ranging 10-21%, they were compacted into a pellet under 150-500 MPa and sintered in air at 1300°C. Even at the relatively low temperature, the maximum density reached 98% TD or higher for the U/(Th+U) ratios of 5-20 mol%. Such high density products survived as firm pellets with a similarly high density of 99% TD during the reduction into (Th, U)O 2 in Ar-H 2 at 1300°C.