The thermal decompositions of both non-activated and mechanically activated aluminum sulfates were studied by thermogravimetry (TG). The structural disorder, the specific surface area (SSA) and the morphology of mechanically activated aluminum sulfates were analyzed by X-ray diffraction (XRD), laser particle-size analyzer, and scanning electron microscopy (SEM), respectively. Thermal analyses results indicated that the initial temperature of thermal decomposition (T i ) in TG curves for mechanically activated aluminum sulfates decreased gradually with increasing the milling time. It was also found that the SSA of mechanically activated aluminum sulfates remained almost constant after a certain milling time, and lattice strains (ɛ) rose but the crystallite sizes (D) decreased with increasing the milling time. These results showed that the decrease of T i in TG curves of mechanically activated aluminum sulfates was mainly caused by the increase of lattice distortions and decrease of the crystallite sizes with increasing the milling time.