The chemical compatibility of sealing glass is of great importance for Solid oxide fuel cell (SOFC). In this work, the interfacial reaction between sealing glass and Cr-containing interconnect alloy is characterized by reacting Cr 2 O 3 powders with a representative SrO-containing glass crystallized by different heat-treatment schedules. The crystalline structure and crystalline content of sealing glass are determined by X-ray diffraction. The results show that the fraction of Cr 6+ decreases from 39.8 ± 1.9% for quenched glass to 8.2 ± 0.4% for glass crystallized at 900 °C for 2 h. In addition, the interfacial reaction can be further reduced with increasing crystallization temperature and time as well as the addition of nucleation agent (TiO 2 ). The formation of some Sr-containing crystalline phases, Sr 2 SiO 4 and Sr(TiO 3 ), contributes to the improvement of chemical compatibility of sealing glass, in agreement with the results of thermodynamic calculations.