An influence of radiation-induced damage on hydrogen isotope retention and transport in a bulk tungsten (W), dense nano-structured W coatings and Eurofer was investigated under well-defined laboratory conditions. Radiation-induced defects in W materials and Eurofer were created by irradiation with 20MeVW ions. Following the damage production, samples were exposed to low-energy deuterium plasma. The deuterium (D) retention in each sample was subsequently measured by nuclear reaction analysis (NRA) for the depth profiling up to 6μm. It was shown that the D retention at radiation-induced damage is almost equivalent for different W grades after irradiation at high enough fluence. The kinetic of D migration and trapping in damaged area as well as recovery of radiation-induced damage were investigated by loading at different temperatures. It was shown that deuterium retention in tungsten in fusion environment will be dominated by radiation-induced effect in a wide range of investigated temperatures, namely, from room temperature to 1100K. Whereas displacement damage produced in Eurofer has less pronounced effect on the deuterium accumulation.