Layered Li(Ni 1 / 3 Co 1 / 3 Mn 1 / 3 )O 2 was prepared by mixed hydroxide method and characterised by means of X-ray diffraction, X-ray photoelectron spectroscopy (XPS), cyclic voltammetry and charge-discharge cycling. The hexagonal lattice parameters obtained for the compound are: a=2.864 and c=14.233 Å. XPS studies show that the predominant oxidation states of Ni, Co and Mn in the compound are 2+, 3+ and 4+, respectively with small content of Ni 3 + and Mn 3 + ions. Initial discharge capacity of 160 mAh/g was obtained in the range 2.5-4.4 V and at a specific current of 30 mA/g of which 143 mAh/g was retained at the end of 40 charge-discharge cycles. At lower current (10 mA/g) and in the voltage window 2.5-4.7 V, discharge capacity of 215 mAh/g is obtainable. From the voltage profile and cyclic voltammetry, the redox processes occurring at ~3.8 and ~4.6 V are assigned to the Ni 2 + / 4 + and Co 3 + / 4 + couples, respectively.