To improve the corrosion resistance and electrical conductivity of Ti-6Al-4V bipolar plates used in polymer electrolyte membrane fuel cells (PEMFCs), a novel electro-conductive Ta2N nanoceramic coating was developed by reactive sputter-deposition using a double cathode glow discharge plasma technique. The microstructure of the coating consisted of fine equiaxed Ta2N grains with an average grain size of ∼13nm, which exhibited a strong (101) preferred orientation. To explore the influence of both pH values and temperatures on the corrosion resistance of the coating, the electrochemical behaviors and electronic properties of passive films grown on the Ta2N coating were systematically investigated using different electrochemical techniques in simulated PEMFC operating environment. It was shown that either increasing the acidity or the temperatures of the solution, the corrosion potential (Ecorr) decreased and the corrosion current density (icorr) increased. At a given temperature or pH value, the Ta2N coating had a higher Ecorr and lower icorr as compared with uncoated Ti-6Al-4V. The results of EIS measurements showed that with increasing temperature or acidity of the solution, the resistance of the passive film (Rp) formed on the Ta2N coating decreased slightly, being of the order of magnitude of 107Ωcm2, which was an order of magnitude higher than that of uncoated Ti-6Al-4V. The interfacial contact resistance (ICR) values were found to increase with increasing pH value or decreasing solution temperature, and the ICR values of the Ta2N coating were markedly lower than that of uncoated Ti-6Al-4V, due to the thinner thickness of passive films. Furthermore, the Ta2N-coated Ti-6Al-4V is more hydrophobic than bare Ti-6A1-4V, which was favorable for both the simplification of water management and improving corrosion resistance in PEMFC operating environment.