Beryllium is one of the main candidate materials both for the neutron multiplier in a solid breeding blanket and for the plasma facing components. That is why the investigation of beryllium behaviour under the typical for fusion reactor loading, in particular under the neutron irradiation, is of a great importance. This paper presents some results of investigation of five beryllium grades (DshG-200, TR-30, TshG-56, TRR, TE-30, TIP-30) fabricated by VNIINM, Russia, and one (S-65) fabricated by Brush Wellman, USA. The average grain size of the investigated beryllium grades varied from 8 to 40 μm, beryllium oxide content was 0.7-3.2 wt.%, initial tensile strength 250-680 MPa. All the samples were irradiated in active zone of SM-3 reactor of 650-700 o C up to the fast neutron fluence (5.5-6.2)x10 2 1 cm - 2 (2.7-3.0 dpa, helium content up to 1150 appm), E>0.1 MeV. Irradiation swelling of the materials was revealed to be in the range of 0.3-1.7%. Beryllium grades TR-30 and TRR having the smallest grain size and highest beryllium oxide content, demonstrated minimal swelling, which did not exceed 0.3% at 700 o C and fluence 5.5x10 2 1 cm - 2 . Mechanical properties and microstructure parameters measured before and after irradiation are also presented.