A new technique for the synthesis of large sheets (>10cm 2 ) of multi-layered graphene is presented. The condensation onto a heated surface (≈650°C) of fumes from the thermal decomposition of asphalt in a ceramic crucible produces carbon films with a metallic sheen. Heating was done by a Fisher burner (natural gas/air) flame and the crucible was covered but exposed to laboratory atmosphere. These films were determined to be multi-layered graphene by scanning electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy (XPS), Raman and infrared spectroscopy and X-ray diffraction. XPS indicates that the films are primarily sp 2 hybridized carbon with small amounts of sp 3 C–H and C–O or C–N functionalities. Based on the D band shift (1593cm −1 ) and the ratio of D band to G band (1354cm −1 ) of 0.93, the Raman spectrum also indicates that the material is sp 2 C with some nanocrystalline features. The infrared spectrum exhibits A 1U (868cm −1 ) and E 1U (1599cm −1 ) stretching of the intralayer bonds of graphene. This form of chemical vapor deposition may be a scalable to give much larger surface areas. Furthermore, the process does not require metal substrates. Deposition onto silica nanosprings and diatomites is demonstrated.