The structure, field-induced strain, polarization and dielectric response of lead-free SrZrO 3 -modified Bi 1/2 (Na 0.80 K 0.20 ) 1/2 TiO 3 (abbreviated as BNKT–SZ100x, with x = 0–0.05) ceramics were investigated. The X-ray diffraction analysis of BNKT–SZ100x ceramics reveals no remarkable change in the crystal structure within the studied composition range. Around critical composition (x = 0.03) at a driving field of 6 kV mm −1 , large unipolar strain of 0.37% (S max /E max = 617) was obtained at room temperature. The ferroelectric and piezoelectric properties of BNKT ceramics were significantly increased at 2 mol%. At x = 0.02, remnant polarization reached a maximum value of 34 μC cm −2 , while the piezoelectric constant (d 33 ) attained maximum value of 190 pC/N. These results indicate that BNKT–SZ100x ceramics can be considered as promising candidate materials for lead-free piezoelectric actuator applications.