New alkaline manganese dioxides were prepared via a single step soft chemistry route, by varying the preparation conditions to adjust the Mn oxidation state. Li capacities as high as 0.85 Li per manganese atom were achieved for some formulations. The lithiated materials, under an initial charge, display a topotactic type reaction within the 2-4.5 V voltage range during the Li (de-)intercalation process, in comparison to the discontinuity in the 3-4 V plateau regions for LiMn 2 O 4 spinel cycling. A slight conversion to the spinel response, however, was observed for materials heated at 300°C. Samples heated at lower temperatures do not exhibit the spinel conversion and provide, in most cases, an appreciable electrochemical response at high cycling rates. This is exemplified by Li 0 . 3 7 K 0 . 0 1 MnO 2 . 0 1 , with a specific capacity of 160 mAh g - 1 at C/1.8 (85 mA g - 1 ).