High temperature filtration from industrial processes offers various advantages in terms of increasing process efficiency, heat recovery and protection of plant installations. Extremely interesting and demanding applications are found in the process industry. This paper describes experimental investigations with a ceramic and two types of metal high temperature filter elements (sintered fleece and woven bags). All three element types have been tested on a laboratory pilot filter with different filtration velocities up to 2.5 m/min and temperatures ranging between ambient and 600°C. Operational differences between ceramic and metal filter media are derived from measurements of the pressure drop behaviour as well as the residual pressure drop of the filter elements. In case of metal filter elements, an additional parameter has to be considered, i.e. the change of media structure in dependence of temperature. For long-term stable operation of high temperature candle filters, a well designed pulse jet regeneration system is essential. Gravimetrically and optically conducted clean gas measurements show for the fleece structures extremely low clean gas concentrations in the range of a few μg/m 3 . Higher values in the range of 10 mg/m 3 were obtained with woven metal bags. Woven metal bags are reasonable cheaper sintered metal fleece elements.Die Hochtemperaturfiltration bietet bei der industriellen Weiterverarbeitung verschiedene Vorteile im Hinblick auf die Erhohung der Verarbeitungseffizienz, die Warmeruckgewinnung und den Schutz von Geraten und Anlagen. In der weiterverarbeitenden Industrie gibt es eine Reihe von interessanten und anspruchsvollen Anwendungsgebieten. Das vorliegende Referat enthalt eine Beschreibung der experimentellen Untersuchungen mit einem Keramik- und zwei Metall-Hochtemperatur-Filterelementen (gesintertes Vlies und Gewebebeutel). Alle drei Arten von Filterelementen sind auf einer Pilotanlage im Labor bei verschiedenen Filtrationsgeschwindigkeiten bis zu 2.5 m/Minute und Temperaturen zwischen Raumtemperatur und 600°C getestet worden. Betriebstechnische Unterschiede zwischen den Keramik- und Metallfiltermedien werden von Messungen des Druckabfallverhaltens sowie des Restdruckabfalls der Filterelemente abgeleitet. In Bezug auf Metallfilterelemente ist ein zusatzlicher Parameter zu berucksichtigen, d.h. die Anderung der Struktur des Filtermediums im Verhaltnis zur Temperatur. Zur Sicherstellung eines auf lange Sicht stabilen Betriebs von Hochtemperatur-Kerzenfiltern ist ein gut ausgelegtes Pulsostrahl-Regenerierungssystem von ausschlaggebender Bedeutung. Gravimetrisch und optisch durchgefuhrte Reingasmessungen zeigen bei Vliesstrukturen ausserst niedrige Reingaskonzentrationen im Bereich von nur wenigen μg/m 3 . Hohere Werte im Bereich von 10 mg/m 3 wurden unter Verwendung von gewebten Metallbeutein erzielt. Gewebte Metallbeutel sind um einiges billiger als gesinterte Metallvlieselemente.La filtration a haute temperature dans les processus industriels offre divers avantages comme l'augmentation de l'efficacite du procede, la recuperation de chaleur et la protection des installations. Des applications extremenent interessantes sont trouvees dans l'industrie des procedes. Cet article decrit les recherches experimentales effectuees avec un ceramique et avec deux types d'elements filtrants metalliques pour hautes temperatures (structure de molleton fritte et poches tissees). Les trois elements ont ete testes sur un filtre pilote de laboratoire a differentes vitesses de filtration jusqu'a 2.5 m/min et a des temperatures variant entre la temperature ambiante et 600°C.Les differences de comportement entre ceramique et medias filtrants metalliques sont deduites des mesures de la montee de la chute de pression ainsi que de la chute de pression residuelle des elements filtrants. Dans le cas des elements filtrants metalliques, un parametre additionnel doit etre considere, a savoir les modifications de la structure du media avec la temperature.Pour un fontionnement stable a long terme des filtres a bougies a haute temperature, un systeme de regeneration a jet pulse de bonne conception est essentiel. Des measures gravimetriques et optiques operees sur gaz epure montrent pour les structures des molletons des concentrations extremement basses de l'ordre de quelques μg/m 3 . Des valeurs plus elevees de l'ordre de 10 mg/m 3 ont ete obtenues avec les poches en metal tisse. Celles-ci sont raisonnablement moins cheres que les elements metalliques frittes.Filtracion a alta temperatura de gases en los procesos industriales ofrece ventajas en terminos de eficiencia creciente, recuperacion de calor, y proteccion de instalaciones de planta. Se hallan aplicaciones muy interesantes y absorbentes en las industrias de proceso.Este articulo presenta investigaciones experimentales con elementos de ceraamico a alta temperatura y dos tipos de metal (vellon fusionado y sacos tejidos). Se han examinado en un laboratorio los tres tipos de elementos en un filtro piloto, con diferentes velocidades de filtracion hasta 2.5 m/min, y temperaturas en el rango entre ambiente y 600°C. Se derivan las diferencias entre medios filtrantes de ceramico y de metal, de medidas de la caida de presion, y de la caida residual de presion de los elementos filtrantes. En el caso de elementos de metal, se debe considerar un pardmetro adicional - el cambio de estructura del medio con temperatura. Una cosa esencial para el funcionamiento firme a la larga de filtros de vela a alta temperatura, es un sistema bien arreglado de regeneracion con chorro pulsado. Medidas por metodos gravimetricos y opticos, de gas limpio dan, con las estructuras vellon, concentraciones muy bajas de gas limpio, en la gama de unos pocos μg/m 3 . Se han obterido valores mas altos (unos 10 mg/m 3 ) con sacos de metal tejido. Los sacos tejidos son was baratos que elementos de metal fusionado.