A grain-selection template was applied to freeze casting to control nucleation of pore-forming crystals and achieve ceramics with highly aligned pore structures. A polymethylsiloxane preceramic polymer was freeze cast with cyclohexane as a solvent to produce dendritic pores in SiOC. Image analysis and permeability measurements were performed to quantify the influence of various templates on sample properties. Results show that the percentage of porosity aligned along the freezing axis increased from 13.9% without a template to 92.6% with an optimal template. The Darcian permeability constant increased by more than 6-fold, from 3.4×10−12 to 2.1×10−11m2.