Laser cladding defect-free coatings on copper is rather difficult. The purpose of this study is to fabricate high quality Co-based alloy coating on copper substrate by laser cladding. Powder preplacement with a thickness of 0.7mm improves the absorptivity of copper substrate to laser effectively and generates defect-free coating. Microstructures, phase constitutions and wear properties are investigated by means of scanning electronic microscopy (SEM) with X-ray energy dispersive microanalysis (EDX), transmission electron microscopy (TEM) and X-ray diffraction (XRD), as well as dry sliding wear test. Experimental results show that α-Co solution, Cr 23 C 6 , Ni 17 W 3 and Cr 4 Ni 15 W are the main phases in the Co-based coating. The Ni-based solid solutions (α-Co, Ni) and (Ni, Cu) are formed at interface, which generate metallurgical bonding by diffusion between Co-based coating and copper substrate. The average microhardness of the coating is 478HV 0.1 . Wear resistance of copper is significantly improved by laser cladding Co-based alloy multilayer coating.