The core–shell structure cathode material Li(Ni 0.8 Co 0.15 Al 0.05 ) 0.8 (Ni 0.5 Mn 0.5 ) 0.2 O 2 (LNCANMO) was synthesized via a co-precipitation method. Its applicability as a cathode material for lithium ion batteries was investigated. The core–shell particle consists of LiNi 0.8 Co 0.15 Al 0.05 O 2 (LNCAO) as the core and a LiNi 0.5 Mn 0.5 O 2 as the shell. The thickness of the LiNi 0.5 Mn 0.5 O 2 layer is approximately 1.25μm, as estimated by field emission scanning electron microscopy (FE-SEM). The cycling behavior between 2.8 and 4.3V at a current rate of 18mAg −1 shows a reversible capacity of about 195mAhg −1 with little capacity loss after 50 cycles. High-rate capability testing shows that even at a rate of 5C, a stable capacity of approximately 127mAhg −1 is retained. In contrast, the capacity of LNCAO rapidly decreases in cyclic and high rate tests. The observed higher current rate capability and cycle stability of LNCANMO can be attributed to the lower impedance including charge transfer resistance and surface film resistance. Differential scanning calorimetry (DSC) indicates that LNCANMO had a much improved oxygen evolution onset temperature of approximately 251°C, and a much lower level of exothermic-heat release compared to LNCAO. The improved thermal stability of the LNCANMO can be ascribed to the thermally stable outer shell of LiNi 0.5 Mn 0.5 O 2 , which suppresses oxygen release from the host lattice and not directly come into contact with the electrolyte solution. In particular, LNCANMO is shown to exhibit improved electrochemical performance and is a safe material for use as an electrode for lithium ion batteries.