Multiblock copolyester (PBS-b-PES) containing poly(butylene succinate) (PBS) and poly(ethylene succinate) (PES) was successfully synthesized by chain-extension of dihydroxyl terminated PBS (HO-PBS-OH) and PES (HO-PES-OH) using 1,6-hexmethylene diisocyanate (HDI) as a chain extender. The chemical structures, molecular weights, crystallization behaviors, thermal and mechanical properties of the copolyesters were characterized by proton nuclear magnetic resonance spectroscopy ( 1 H NMR), gel permeation chromatography (GPC), differential scanning calorimetry (DSC), thermogravimetry analysis (TGA), wide-angle X-ray diffraction (WAXD), tensile testing and hydrolytic degradation. High-molecular-weight copolyesters with M w more than 2.0×10 5 gmol −1 were easily obtained through chain-extension. The copolyesters showed a single glass transition temperature (T g ) which increased with PES content. The melting point temperature (T m ) and relative degree of crystallinity (X c ) of the copolyesters decreased first and then increased with PES content. The copolyesters manifested excellent mechanical properties, for example, PBS 5 -b-PES 5 had fracture stress of 61.8MPa and fracture strain of 1173%. The chain-extension reaction provided a very effective way to produce high molecular weight multiblock copolyesters.