The Pr2Fe17 compound is a potential candidate for low cost magnetocaloric materials with a significant relative cooling power (RCP) around room temperature (280K). In this work, we present the results of the substitution of dysprosium for praseodymium and of the substitution of aluminum for iron in Pr2Fe17. The polycrystalline Pr2Fe17, Pr1.75Dy0.25Fe17 and Pr2Fe16.75Al0.25 were prepared by arc melting under a high purity argon and homogenized at 1373K to minimize the amount of other possible impurity phases. All the samples crystallize in the rhombohedral Th2Zn17 type structure. The lattice parameter increases with the Al and Dy content. The Curie temperature increases with Dy content and Al content. The magnetic entropy change ΔSm was estimated from isothermal magnetization curves for all samples.