Ultra thin platinum films were grown by dc magnetron sputtering on thermally oxidized Si (100) substrates. The electrical resistance of the films was monitored in situ during growth. The coalescence thickness was determined for various growth temperatures and found to increase from 1.1nm for films grown at room temperature to 3.3nm for films grown at 400°C. A continuous film was formed at a thickness of 2.9nm at room temperature and 7.5nm at 400°C. The room temperature electrical resistivity decreases with increased growth temperature, while the in-plain grain size and the surface roughness, measured with a scanning tunneling microscope (STM), increase. Furthermore, the temperature dependence of the film electrical resistance was explored at various stages during growth.