A solution process was used to grow epitaxial La 2 Zr 2 O 7 (LZO) buffer layers on roll-textured Ni (100) substrates to produce YBa 2 Cu 3 O 7 - δ (YBCO)-coated conductors. The LZO precursor solution was prepared by an all alkoxide sol-gel route using mixed metal methoxyethoxides in 2-methoxyethanol. The partially hydrolyzed solution was either spin-coated or dip-coated onto the textured Ni substrates. The amorphous thin film was then heat treated at 1150 o C under (96%)Ar/(4%)H 2 atmosphere for 1 h. X-ray diffraction (XRD) of the buffer layer indicated a strong c-axis orientation on the Ni (100) substrate. The LZO (222) pole figure revealed a single cube-on-cube texture. SEM images of the LZO buffer layer showed a dense microstructure without cracks. The YBCO deposited on the sol-gel LZO-buffered Ni substrates with sputtered YSZ and CeO 2 top layers had a critical current density of 480,000 A/cm 2 at 77 K and self-field.