Polylactic acid (PLA), dicalcium phosphate dihydrate (DCPD) and/or hydraulic calcium silicate (CaSi) have been used to prepare highly-porous scaffolds by thermally induced phase separation technique (TIPS). Three experimental mineral-doped formulations were prepared (PLA-10CaSi, PLA-5CaSi-5DCPD, PLA-10CaSi-10DCPD). Pure PLA scaffolds constituted the control group.Scaffolds were tested for their chemical-physical and biological properties, namely calcium release, alkalinizing activity, surface microchemistry and micromorphology by ESEM, apatite-forming ability by EDX, micro-Raman and IR spectroscopy, thermal properties by differential scanning calorimetry, mechanical properties by quasi-static parallel-plates compression testing, porosity by a standard water-absorption method and direct-contact cytotoxicity.All mineral-doped scaffolds released biologically relevant ions (biointeractive). A B-type carbonated apatite layer (thickness decreasing along the series PLA-10CaSi-10DCPD>PLA-10CaSi>PLA-5CaSi-5DCPD>PLA) was detected on the surface of all the 28d-aged scaffolds.Surface pores of fresh scaffolds ranged from 10 to 20μm in pure PLA to 10–100μm in PLA-10CaSi. An increase in porosity was detected in 28d–aged pure PLA scaffolds (approx. 30% of material loss with decrease of the PLA chain length); differently, in mineral-doped scaffolds, the PLA degradation was balanced by deposition/nucleation of apatite. All scaffolds showed absence of toxicity, in particular PLA-10CaSi-10DCPD.The designed scaffolds are biointeractive (release biologically relevant ions), nucleate apatite, possess high surface and internal open porosity and can be colonized by cells, appearing interesting materials for bone regeneration.