(MnO) x ·(P 2 O 5 ) 40 ·(ZnO) 60−x glasses containing different concentrations of MnO ranging from 0 to 20mol% were prepared by the melt-quenching technique. The samples had a fixed P 2 O 5 content of 40mol% and the MnO:ZnO ratio was varied. The thermal, structural and magnetic properties of these glasses were investigated by means of differential thermal analysis (DTA), electron paramagnetic resonance (EPR) and magnetic susceptibility measurements. Compositional dependence of the glass transition (T g ), crystallization (T p ) and melting temperatures were determined by DTA investigations. From the dependence of the T g on the heating rate (a), the activation energy of the glass transition (E g ) was calculated. The fragility index (F) for the studied glasses was determined to see whether these materials are obtained from kinetically strong-glass-forming (KS) or kinetically fragile-glass forming (KF) liquids. The EPR spectra of the studied glasses revealed absorptions centered at g≈2.0, 3.3 and 4.3. The compositional variations of the intensity and line width of these absorption lines was interpreted in terms of the variation in the concentration of the Mn 2+ and Mn 3+ ions in the glass and the interaction between the manganese ions. EPR and magnetic susceptibility data reveal that both Mn 2+ and Mn 3+ ions are present in the studied glasses, their relative concentration being dependent on the glass composition. Magnetic susceptibility data reveal an antiferromagnetic interaction between the manganese ions for the glasses containing 20mol% MnO.