Al 2 O 3 -based compressive seals were fabricated by tape casting with Al 2 O 3 and 0–30 wt% aluminum powders, and their sealing effectiveness, thermal cycle stability between 200 and 750 °C and applicability in planar intermediate temperature solid oxide fuel cells were evaluated. The results indicate that increasing the aluminum content from 0 to 30 wt% in the seals decreases the leakage rate and increases the thermal cycle stability under various inlet gas (N 2 ) pressures of 3.5, 7.0 and 10.5 kPa. Especially, with the seal containing 30 wt% of aluminum (ACS3), the initial leakage rate was below 0.03 sccm cm −1 under an inlet pressure of 10.5 kPa, and the leakage rates during 96 thermal cycles were below 0.04 sccm cm −1 under the same inlet gas pressure. The interfaces in the interconnect/seal/cell assembly with the ACS3 seal retained integrity after 50 thermal cycles, demonstrating the applicability of the Al 2 O 3 -based compressive seals in the planar intermediate temperature SOFCs.