Adhesion to thermoplastic olefin (TPO) substrates is strongly influenced by the type and amount of solvent contained within paint applied. Morphological changes in the TPO substrate are accomplished in the presence of solvent from the topcoat and vary depending upon paint bake times and temperatures. These morphological changes at and near the surface of TPO affect not only the paint adhesion to the substrate but also the cohesive integrity of the painted plastic composite. This paper attempts to delineate the influence of paint and paint processes on the adhesion/cohesion and mechanical properties of coated TPO parts, in particular, the performance of 2K topcoated TPO substrates under thermal shock conditions. It was found that the most important attribute contributing to thermal shock resistance of painted TPO parts was the bake temperature of the topcoat. A temperature of 250 o F in either the adhesion promoter bake or the topcoat bake is necessary to afford acceptable thermal shock performance. It is postulated that the rearrangement of poly(propylene) crystallites at the uppermost surface of the TPO under a 250 o F bake accounts for the increased cohesive strength of the painted composite.