Poly(trimethylene terephthalate) (PTT)/poly(ethylene naphthalate) (PEN) blends were miscible in the amorphous state in all of the blend compositions studied, as evidenced by a single, composition-dependent glass transition temperature (T g ) observed for each blend composition. The variation in the T g value with the blend composition was well predicted by the Gordon–Taylor equation, with the fitting parameter being 0.57. The cold-crystallization peak temperature decreased with increasing PTT content, while the melt-crystallization peak temperature decreased with increasing amount of the minor component. The subsequent melting behavior after both cold- and melt-crystallization exhibited melting point depression, in which the observed melting temperatures decreased with increasing amount of the minor component. During melt-crystallization, both components in the blends crystallized concurrently just to form their own crystals. The blend with 60% w/w of PTT exhibited the lowest total apparent degree of crystallinity.