Hydrogen evolution reaction (HER) is considered to be one of the most promising strategies to create hydrogen. Recently, searching high-efficient, stable, and earth-abundant electrocatalysts to replace precious metals for practical utilizations of HER is attracting more and more attentions. Herein, novel molybdenum carbide nanobelts containing Mo of high-valence state derived from MoO3-ethylenediamine inorganic/organic hybrid precursors are successfully synthesized via a facile one-pot pyrolysis method. The molybdenum carbide nanobelts are characterized using XRD, SEM, TEM and XPS. Moreover, the high-valence state Mo and their relative content in the molybdenum carbide nanobelts can be identified by XPS. The high-resolution XPS spectra of Mo 3d indicates in the molybdenum carbide nanobelts the proportion of high-valence state Mo in active Mo components is 51.3%. More importantly, the as-synthesized products exhibit excellent electrocatalytic activity for HER with a low onset overpotential of 50 mV and a small Tafel slope of 49.6 mV dec−1 in acidic medium (0.5 M H2SO4). Besides, the catalysts require only overpotentials of 143 and 234 mV to achieve current densities of 10 and 220 mA cm−2, respectively. Furthermore, they also exhibit good durability after 2000 cycles and constant current density test. Such excellent electrocatalytic HER performance can be ascribed to the high intrinsic activity of high-valence state Mo in Molybdenum Carbide. Synthesizing molybdenum carbide with high-valence state Mo electrocatalysts for HER will open up an exciting alternative avenue to acquire outstanding HER electrocatalytic activity.