The aim of this study was investigation of changes in the modified near-surface layer on the NiTi shape memory alloy, caused by ion implantation as well as their influence on the mechanical and shape memory properties of this material. Surface of NiTi has been modified by nitrogen ion beam at several fluences 1×10 17 cm −2 , 1×10 18 cm −2 and 2×10 18 cm −2 at the energy 50keV. The effect of implantation parameters on surface characteristics and wear properties was investigated using dry-sliding-wear test, depth sensing indentation test and scanning profilometry method. The experimental results have shown how the ion implantation treatment can change the original surface: reducing Ni content in the surface, increasing the surface hardness (furthermore, the hardness improvement extended to the regions much deeper than the implanted layer), and improving the sliding wear resistance. The experimental results of surface treatment conditions and mechanical properties of the modified NiTi alloys are compared, analyzed and discussed in this paper.