Smectites were synthesized from gels containing the cations: Si 4 + , Al 3 + , Fe 2 + , Mg 2 + , Na + or Si 4 + , Al 3 + , Fe 2 + , Na + . Gels were prepared at 25 o C in reducing conditions (glove box with nitrogen circulation, oxygen partial pressure = 10 - 6 atm). During synthesis, performed at 200 o C for 41 days in teflon coated steel bombs put in a furnace, gas exchanges occur between bombs and laboratory atmospheres. The synthetic smectites are ferric beidellites with a Fe 2 + Fe t o t a l ratio ranging from 0 to 0.2. The octahedral Fe 2 + ions in smectites appear stable over several months.Des smectites ont ete synthetisees a partir de gels contenant les cations Si 4 + , Al 3 + , Fe 2 + , Mg 2 + , Na + ou Si 4 + , Al 3 + , Fe 2 + , Na + , prepares en milieu reducteur a 25 o C (boite a gants a circulation d'azote, pression partielle d'oxygene = 10 - 6 atm). Durant la synthese realisee a 200 o C pendant 41 jours dans des reacteurs en acier chemise teflon, places dans une etuve, des echanges de gaz se font entre les reacteurs et l'atmosphere du laboratoire. Les smectites synthetisees sont des beidellites ferriferes, dont le rapport Fe 2 + Fe t o t a l varie de 0 a 0,2. Les ions Fe 2 + stabilises dans les octaedres des smectites ne s'oxydent pas au bout de plusieurs mois.