The aim of the work was to investigate the possibilities of shaping the properties of TiB2 coatings by doping with tungsten, which create hard boron phases (e.g., WB2 , WB4 , and W2 B5). The coatings were produced by a DC magnetron sputtering processes using two circular magnetrons (M1, M2) equipped respectively with M1 - target TiB2 , and M2 - target W. Ti-W-B coatings with different tungsten contents (3%, 6%, 10%) were prepared for which the reference coating was the TiB2 coating. The work studied chemical composition (WDS), mechanical properties (Nano Hardness Tester), and the microstructure of coatings (SEM). It has been shown that doping TiB2 coating with tungsten significantly changes their microstructure and brittle fracture mechanism. According to the authors, the Ti-W-B coatings which were obtained show promising results regarding the prognosis of increasing their resistance to abrasion, erosion, and brittle cracking, if they are paired with the appropriate substrate material.
Celem pracy było zbadanie możliwości kształtowania właściwości powłok TiB2 poprzez domieszkowanie wolframem, który tworzy twarde fazy z borem (np. WB2 , WB4, W2 B5). Powłoki wytwarzano w procesie stałoprądowego rozpylania magnetronowego z wykorzystaniem dwóch magnetronów kołowych wyposażonych odpowiednio: M1 - target TiB, M2 - target W. Wytworzono powłoki Ti-W-B o różnej zawartości wolframu (3%, 6%, 10%), dla których powłoką referencyjną była powłoka TiB2 . W pracy badano skład chemiczny (WDS), właściwości mechaniczne (Nano Hardness Tester) oraz budowę wewnętrzną powłok (SEM). Wykazano, że domieszkowanie powłok TiB2 wolframem istotnie zmienia ich mikrostrukturę oraz mechanizm kruchego pękania. W ocenie autorów wytworzone powłoki Ti-W-B wykazują obiecujące wyniki dotyczące prognozowania wzrostu ich odporności na zużycie ścierne, erozyjne oraz kruche pękanie, jeśli będą sparowane z odpowiednim materiałem podłoża.