The microstructure analysis of Fe-Al intermetallic coating deposited by detonation-gaseous spraying (DGS) on the 045 carbon steel substrate was presented in the paper. The microstructure was investigated using scanning (SEM) and transmission (TEM) electron microscopy, as well as selected area electron diffraction (SAED) techniques. The chemical concentration in microareas was revealed using the energy dispersive X-ray (EDS) spectroscopy technique. The TEM technique was applied to the analysis across the coating as well as close to the coating/substrate interface. The vicinity of the substrate was composed of an amorphous phase and columnar crystals as a result of rapid solidification of the partially melted FeAl powder. The Fe3Al phase was identified inside the coating, while at its surface Fe2Al5, Fe3Al and FeCrAl phases were found. Their occurrence and also the FeAl2O4 phase and aluminium oxide were confirmed by the X-ray diffraction method.
W pracy przedstawiono analizę mikrostruktury powłoki międzymetalicznej faz typu Fe-Al naniesionej przez natryskiwanie detonacyjno-gazowe (DGS) na podłoże ze stali węglowej 045. Analizę tą przeprowadzono na podstawie badań metodą skaningowej (SEM) i transmisyjnej mikroskopii elektronowej(TEM). Metodą TEM analizowano budowę powłoki zarówno w głębi jak i w pobliżu granicy z podłożem. W sąsiedztwie podłoża stwierdzono fazę amorficzną oraz kryształy kolumnowe jako rezultat szybkiego krzepnięcia nadtopionej części proszku FeAl. W głębi powłoki zidentyfikowano fazy Fe3Al, zaś na jej powierzchni fazy Fe2Al5 i Fe3Al oraz FeCrAl. Występowanie tych faz oraz FeAl2O4 i tlenku glinu potwierdzono metodą dyfrakcji rentgenowskiej.