The purpose of this work was to iiwestigate microstructure of a heat affected zonę (HAZ) of aluminium alloy 2017A-T4 to determine its effect on corrosion behaviour of this alloy. The microstructure in HAZ was simulated by local rapid heating of the alloy and immediate cooling in air. Corrosion testing was performed by exposure to marinę onshore atmosphere. The microstructure examinations were carried out using light microscopy, scanning electron microscopy, X-ray energy dispersion and X-ray diffraction analysis. A elear correlation was found between microstructure and susceptibility to intercrystalline and pitting corrosion in the zones heated to temperatures below, close and above the solvus line.
Celem pracy było zbadanie zmian mikrostruktury w strefie wpływu ciepła (SWC) stopu 2017A-T4 oraz określenie jej wpływu na przebieg korozji stopu. Zmiany mikrostruktury analogiczne do zmian w SWC połączeń spawanych otrzymano przez lokalne, szybkie nagrzanie jednego końca rurowej próbki i natychmiastowe ochłodzenie w powietrzu. Badania korozyjne przeprowadzono poddając stop ekspozycji w atmosferze klimatu morskiego, w głębi lądu. Badania mikrostruktury przeprowadzono przy zastosowaniu technik mikroskopii świetlnej, elektronowej mikroskopii skaningowej, analizy dyspersji energii promieniowania rentgenowskiego oraz analizy dyfrakcji rentgenowskiej. Znaleziono wyraźną korelację pomiędzy mikrostrukturą a podatnością stopu na korozję międzykrystaliczną i wżerową w strefach nagrzania do temperatury niższej, bliskiej i wyższej od linii granicznej rozpuszczalności.