Cu-Ni-Zn and Co-Ni-Zn alloys were prepared in quartz tubes using pure components. The specimens were polished and their phase compositions were determined by electron probe microanalyses. The phase boundaries in the zinc-rich corners of the Cu-Ni-Zn and Co-Ni-Zn systems have been investigated at 868 K. The phase relations at higher temperatures (1178 and 1080 K) are verified as well. Ternary compounds non-related with the binary systems have not been found. The ternary extension of the Cu-Zn gamma-phase contains up to 4 at.% Ni. The location of the phase boundaries of the ternary liquid and ?-phases have been precised for both ternary systems. Isothermal sections of the phase diagrams Cu-Ni-Zn (at 868 K) and Co-Ni-Zn (at 868 K and 1083 K) have been constructed using the experimental data obtained in this work and literature data about the end binary systems.
Badane stopy Cu-Ni-Zn i Co-Ni-Zn przygotowano z czystych metali przez stopienie w ampulach kwarcowych pod próżnią. Skład fazowy polerowanych próbek tych stopów określona za pomocą mikroanalizy elektronowej. Dla bodatych w Zn części układów fazowych Cu-Ni-Zn i Co-Ni-Zn określono granice fazowe dla temperatury 868K. Relacje fazowe zweryfikowano także dla wyższych temperatur: 1083 i 1178K. Nie stwierdzono występowania niezwiązanych z fazami dwuskładnikowymi, osobnych faz trójskładnikowych. Okreslono maksymalną rozpuszczalność Ni w fazie Cu-Zn-epsilon na ok. 4%at. Sprecyzowano połozenie granic fazowych pomiędzy roztworem ciekłym, a fazą gamma w obu układach trójskładnikowych. Wykorzystując dane własne i dane literaturowe dla układów dwuskładnikowych skonstruowano izotermiczne przekroje układów fazowych Cu-Ni-Zn dla temperatury 868K i Co-Ni-Zn dla 868 i 1083K.