A multi-walled carbon nanotube/l-butyl-3-methylimidazolium tetrafluoroborate/chitosan (MWCNT/IL/CS) composite film - modified glassy carbon electrode (OCR) was fabricated by spin coating. Electrochemical behavior of tinidazole at the composite film electrode was investigated applying voltammetry. A distinct reduction peak located at ca -0.688 V <\ was observed during potential cycling in the range from 0.200 V to -1.00 V. Compared to its voltammetric behavior on bare GCE, the reduction peak potential of tinidazole was shifted positively and the peak current significantly increased. All experimental parameters for electrochemical determination of tinidazole were optimized. The detection limit and linear calibration range were 1.OO.x 10-7mol L-7(S/N = 3) and 3.00x 10-7to 2.00x 10-5mol L-1, respectively. In addition, using the proposed film electrode determination of tinidazole in real tablets was carried out with satisfactory results.
Przebadano woltamperometrycznie tynidazol z użyciem elektrody z węgla szklistego zmodyfikowanej warstwą kompozytową składającą się z wielościennych nanorurek węglowych, tetrafluoroboranu l-bulylo-3-metyloimidazolu i chitozanu. Wyraźny pik redukcji pojawił się przy -0,688 V. Porównując ten pik do piku uzyskanego na zwykłej elektrodzie z węgla szklistego stwierdzono, że przesunął się on w kierunku potencjałów dodatnich i znacznie wzrósł. Zoptymalizowano wszystkie parametry do elektrochemicznego oznaczania tynida-zolu. Granica wykrywalności wyniosła 1.00 x 10-7mol L-1(S/N = 3), a zakres liniowości krzywej kalibracyjnej określono na 3 x 10-7-2x 10-5mol L-1. Opracowaną metodę użyto z powodzeniem do oznaczania tynidazolu w tabletkach.