The 6xxx series aluminum alloys (Al-Mg-Si) with a wide range of properties are extensively used in engineering structures and architectural applications. Mechanical properties of 6xxx series alloys depend on their chemical composition and heat treatment parameters. Increasing Si concentration in chemical composition of 6xxx series alloys increases strength in the T6 tempers. Strengthening effectiveness of the alloys depends upon the extent of transitiona B" precipitation that increases with increasing of B-Mg2Si content in the aluminium alloys. In this work 6061, 6063 and 6082 alloys were subjected to solution heat treatment at 565°C for 12 h, and then water quenched followed by artificial aging at 150°C up to 190 h. Hardness and tension tests were used to evaluate the mechanical properties. The highest mechanical properties connected with a good plastic properties was achieved for 6061 alloy with the highest volume fraction of B-Mg2Si.
Stopy aluminium grupy 6xxx (Al-Mg-Si) są szeroko stosowane w wielu gałęziach przemysłu. Właściwości mechaniczne stopów grupy 6xxx zależą m.in. od składu chemicznego, jak również parametrów prowadzonej obróbki cieplnej. Zwiększenie zawartości Si w stopach 6xxx prowadzi do wzrostu ich wytrzymałości w stanie T6. Stopień umocnienia zależy od objętości względnej faz przejściowych B" i B' i równowagowej fazy !-Mg2Si. W celu określenia oddziaływania składu chemicznego oraz warunków prowadzenia procesu umacniania wydzieleniowego na właściwości mechaniczne, stopy aluminium 6061, 6063, 6082 przesycono w temperaturze 565°C przez 12 h i chłodzono w wodzie, a następnie starzono sztucznie w temperaturze 150°C przez 190 h. Prowadzono pomiary twardości w określonych odstępach czasu oraz wykonano próbę statyczną rozciągania. Ustalono, że najwyższe właściwości mechaniczne przy zachowaniu wysokiej plastyczności wykazuje stop 6061 o największej objętości względnej fazy B-Mg2Si.