The paper presents the results of studies on the effect of heat treatment and cyclic deformation on the properties of the magnesium alloy AZ91. The alloy was subjected to heat treatment by solutioning and ageing (420 °C/24 h/powietrze+210 °C/4 h/powietrze) and then to cyclic uniaxial zero-start pulsating loads. The maximal amplitudes of cyclic loads 54 and 74 MPa were lower than the offset yield strength of the alloy. The microstructure of the alloy is presented, while the properties of the alloy before and after cycling loading (up to 50 and 70 cycles) are determined by measurements of residual stress made by the X-ray method of sin2fi. It has been found that cyclic deformation causes the strengthening of the alloy AZ91. The strengthening of the alloy is found to increase with increasing loading amplitude and number of cycles, with the greatest strengthening effect occurs in the first three loading cycles.
W pracy przedstawiono wyniki badań wpływu obróbki cieplnej i cyklicznego odkształcania na własności stopu magnezu AZ91. Stop poddano obróbce cieplnej przesycania i starzenia (420 stopni C/24 h/powietrze+210 stopni C/4 h/powietrze) a następnie cyklicznym jednoosiowym obciążeniom odzerowo tętniącym. Maksymalne amplitudy cyklicznych obciążeń 54 i 74 MPa były niższe od umownej granicy plastyczności stopu. Przedstawiono mikrostrukturę stopu, a własności stopu przed i po cyklicznym obciążaniu (po 50 i 70 cyklach) określono przez pomiary naprężeń szczątkowych metodą rentgenowską sin2 fi. Stwierdzono, że cykliczne odkształcanie powoduje umocnienie stopu AZ91. Wykazano, że umocnienie stopu zwiększa się wraz ze wzrostem amplitudy obciążania oraz z liczbą cykli, a największy efekt umocnienia występuje w pierwszych trzech cyklach obciążania.